9GRAND 5D ML Multilayer Zirconia

Health Canada Licensed. 

Medisco – Grand ML™ Multilayered Dental Zirconia used for dental restoration using open CAD/CAM systems, 98mm

5 Layer Multi-layer, extra-translucent ZrO₂ with integrated tooth colour gradient. For the fabrication of fully anatomical anterior or posterior restorations with special vitality. High breaking strength and fracture toughness. For open CAD/CAM systems of 98mm diameter. Do not require Liquid for coloring.

    For the fabrication of Full Contour Crowns, Full Contour Bridges, Coping & Frameworks, Full Arches. Medical device Class IIa.

    Superior Strength: >1000 – 1290 MPa

    Superior Translucency: 43% – 47%

    • Health Canada Licensed
    • 5 Layers
    • Strength > 1000-1290 MPa
    • Superior Translucency
    • Natural Appearance
    • Multilayered – 5 Layers
    • 16 Shades
    Physical data:
      CTE 10.5 ± 1.0 x 10⁻⁶K⁻¹ (25-500 °C); density after sintering 6.07 ± 0.01 g/cm³; bending strength (3-point bending test) > 1200 MPa; sintering temperature 1400-1580 °C, recommended 1530 °C; translucency 43% – 47% %.
    Composition in %:
      ZrO₂ + HfO₂ + Y₂O₃ ≥ 99; Y₂O₃ 4.5-6; Al₂O₃ ≤ 0.5; other oxides ≤ 0.5.

    Available in Sizes

    • 98 x 12 mm
    • 98 x 14 mm
    • 98 x 16 mm
    • 98 x 18 mm
    • 98 x 20 mm
    • 98 x 22 mm
    • 98 x 25 mm

    Available in 16 Colors 

    • A1,A2,A3,A3.5,A4
    • B1,B2,B3,B4
    • C1,C2,C3,C4
    • D2,D3,D4 
    • BL1

     

    Feature

    Grand 5D ML™ Multilayer Zirconia

    Product Type

    5-layer, extra-translucent zirconia with integrated tooth color gradient

    Translucency

    43%-47%

    Strength

    1000–1290 MPa

    Layers

    5 layers

    Indications

    Full contour crowns, full contour bridges, coping & frameworks, full arches

    Shades Available

    16 shades (A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4, BL1)

    Sintering Temperature

    1400–1580°C (recommended 1530°C)

    Sintering Density

    6.07 ± 0.01 g/cm³

    Coefficient of Thermal Expansion (CTE)

    10.5 ± 1.0 x 10⁻⁶ K⁻¹ (25–500°C)

    Composition

    ZrO₂ + HfO₂ + Y₂O₃ ≥ 99%; Y₂O₃ 4.5–6%; Al₂O₃ ≤ 0.5%; other oxides ≤ 0.5%

    Health Canada Licensed

    Yes

    Medical Device Class

    IIa